Welding Wire Storage Procedure

Temperature 17 27 c relative humidity.

Welding wire storage procedure.

Checklist during welding. Storage times should be kept as short as possible. Storage handling packaging storage for mild and low alloy steel mig and subarc wires wire package type 1 wire storage conditions for all welding applications any type protect from rain or snow. Tubular wire packed in the original foil and cardboard box or drum require controlled warehouse conditions such as.

Keen spooled wire ovens fcaw mig saw para español clique aquí. Older wire should be redried before use. When stick electrodes absorb moisture from the atmosphere they must be dried in order to restore their ability to deposit quality welds. Temperature 27 37 c relative humidity.

Storage procedure electrodes fluxcored wire flux moisture is still the main enemy for welding consumables. Wire for tig gtaw welding should be protected from dust and airborne contamination after removal from the packaging. Unopened hermetically sealed containers provide excellent protection in good storage conditions. Storage exposure to a humid environment with only a relative thin plastic foil shall be prevented.

Low hydrogen electrodes must be dry to perform properly. Welding consumables should be stored in their original unopened packaging in an area shielded from the elements. Made in the usa and ruggedly constructed keen s fcaw flux cored wire reel storage ovens and mig metal inert gas welding wire storage ovens are available in a wide variety of capacities to suit the most rigorous welding operations. Adequate storage handling and re conditioning of electrodes vary according to type.

The minerals being used to form the slag that covers the weld pool are highly hygroscopic and should be taken very seriously for submerged arc powder and covered stick electrodes. Whenever possible the first in first out principle should be adopted. Flux cored wire should not be stored for more than 5 years. Wire should be stored at ambient conditions of temperature and humidity and dusty areas should be avoided when wire is not enclosed in some type of dust protecting packaging or equipment.

Moisture resistant electrodes with an r suffix have a high resistance to coating moisture pick up. These parameters include items such as wire feed speed voltage electrical stickout welding technique welding progression travel and push angles shielding gas adequate preheat and interpass temperature if required etc. Electrodes with too much moisture may lead to cracking or porosity. Opened cans or electrodes should be stored in a cabinet at 120 150 c 250 300 f.

Storage for submerged arc flux flux package type 1 flux storage conditions for. Do not use wire with visible signs of rust.